The salt spray (or salt fog) test is a standardized and popular corrosion test method, used to ASTM B was the first internationally recognized salt spray standard, originally published in Other important relevant standards are. Designation: B – 07a Standard Practice for Operating Salt Spray (Fog) Apparatus1 This standard is issued under the?xed designation B. ASTM B Testing, also known as a Standard Practice for Operating Salt ASTM B Testing requires controls over many operational parameters such as: .

Author: Vushakar Kazirn
Country: Bhutan
Language: English (Spanish)
Genre: Life
Published (Last): 27 March 2006
Pages: 402
PDF File Size: 16.91 Mb
ePub File Size: 11.38 Mb
ISBN: 918-5-37940-491-4
Downloads: 16669
Price: Free* [*Free Regsitration Required]
Uploader: Nakora

Take about a mL sample of the salt solution as prepared at room temperature, boil gently for 30 s, cool, and determine the pH. All necessary material for determining corrosiovity test panels, chemicals and other b117-007a you can buy in our webshop.

Preparation of Test Specimens 6. This is followed by 2. Heating Blocks for Evaporators. This standard has been approved for use by agencies of the Department of Defense. This b117-7a followed by 3. The chamber has the following features: The salt spray or salt fog test is a standardized and popular corrosion test method, used to check corrosion resistance of materials and surface coatings.

SaliCORR® ASTM B117 Sodium Chloride 5 kg bags

It is preferred that control panels be provided that bracket the expected test specimen performance. Requirements are agreed between customer and manufacturer. Test specimens are placed in an enclosed chamber and exposed to a continuous astmm spray of salt water solution, prepared in accordance with the requirements of the test standard and acidified to pH 3. Most commonly, the time taken for oxides to appear on the samples under test is compared to expectations, to determine whether the test is passed or failed.


Salt spray test – Wikipedia

This produces a corrosive environment of dense salt water fog also referred to as a mist or spray in the chamber, so that test samples exposed to this environment are subjected to severely asgm conditions. Spraying asstm test solution. Unit for filtering compressed air. ASTM does not address this issue, but ISO does not recommend it and if it is to be done, advocates a thorough cleaning. If there is a minimum volume required by a particular salt spray test standard, this will be clearly stated and should be complied with.

Suitable apparatus which may be used bb117-07a described in Appendix X1. NOTE 7—If the tower is run outside of these suggested temperature and pressure ranges to acheive proper collection rates as described in The procedure involves the exposure of steel test panels and the determination of their mass losses in a speci?

SAL 400-FL

Test solution tank L. The principle application of the salt spray test is therefore enabling quick comparisons to be made between actual and expected corrosion resistance.

Each set point and its tolerance represents an operational control point for equilibrium conditions at a single location in the cabinet which may not necessarily represent the uniformity of conditions throughout the cabinet. The first prerequisite for your test chamber to operate properly is that it v117-07a regularly serviced and well maintained.

  AWWA C200-97 PDF

However, in order to obtain reliable results additional requirements must be met.

Astk of Exposure Water plant for supply of demineralised water. Salt spray testing is an accelerated corrosion test that produces a corrosive attack to coated samples in order to evaluate mostly comparatively the suitability of the coating for use as a protective finish.

By using this site, you agree to the Terms of Use and Privacy Policy. ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard. Failure to meet this requirement implies instability in the chemical process of the pre-treatment, or the paint quality, which must be addressed immediately, so that the upcoming batches are of the desired quality.

Conditions in the Salt Spray Chamber This test can be used to test the relative resistance to corrosion of coated or uncoated aluminium alloys and other metals, when exposed to a changing climate of acidified synthetic seawater spray, followed by a high humidity, both at an elevated temperature.

Thus, the level of the solution in the salt reservoir must be maintained automatically to ensure uniform fog delivery during the test. Halides Bromide, Fluoride, and Iodide other than Chloride shall constitute less than 0. Once a year the corrosivity of the salt spray test chamber has to be checked.